Windsor Stevens VHR-115 is a dense, rigid material produced in multi-ply construction from unbleached kraft pulp and acrylic polymer. It has excellent dielectric and mechanical strengths, low water absorption and is free of conducting particles, chemical impurities and foreign matter. Its chemical cleanliness accounts for its excellent aging characteristics in air up to 115°C.
Windsor Stevens VHR-115 can be used in numerous coil, transformer, motor, electrical hardware and electronic applications where excellent dielectric and physical strengths are required.
Windsor Stevens VHR-115 is approved by Underwriters Laboratories reference E-31556(M) electrical use at 115°C and mechanical at 110°C.
Windsor Stevens VHR-115 is available in sheets, strips, mill rolls and slit rolls in thicknesses from .010” to .062”.
PHYSICAL, ELECTRICAL AND CHEMICAL PROPERTIES:
|Fiber Content||100% Unbleached Kraft Wood Pulp|
|Ash Content (Max.)||.75%|
|pH Water Extract||6.5 – 7.5|
|Moisture Content||7.0% Avg.|
|Water Absorption % change in wgt. 24 hrs max|| 2 hours 50%
24 hours 60%
|Standard Thickness, ± 7%||Inches||.010||.015||.020||.025||.031||.062|
|Apparent Density, (Air Dry), ± 7%||g/cc||1.05||1.05||1.05||1.05||1.05||1.05|
|Weight, (Air Dry), ± 7%||lbs./sq. ft.||.054||.082||.109||.136||.169||.338|
|Dielectric Strength, (Avg.) grams AC, 25˚C||Volts/mil||250||250||250||250||250||250|
|Tensile Strength, (Avg.)||MD lbs./In.||200||305||425||540||660|
|Burst Strength, (Avg.)||lbs./sq. in.||150||250||375||460||550||900|
|Tear Strength, (Avg.) grams||MD||255||450||615||830||950|
Click here to download the VHR-115 Spec Sheet.
Click here to download the VHR SDS Sheet.
“Values shown are typical, are not guaranteed, nor to be used for specifications without approval.”
NOTICE: The above information and data are believed to be accurate and reliable. Windsor Stevens assumes no responsibility for end-use applications and no performance warranty is expressed or implied.